E.V.F -- V.O.D -- C.C. Bloom -- Hot Rolling Billet(1st) -- Hot Rolling F/Bar(2nd)-- Cold Rolling -- Heat Treatment(Solution Annealing)-- Picking -- Levelling -- Surface Grinding & Polishing -- Machined F/Bar
Cold Rolling M/C
Grinding & Polishing M/C
Free cutting stainless steel flat bat for watch case.
Grade:
-
E.V.F -- V.O.D -- C.C. Bloom -- Hot Rolling Billet(1st) -- Hot Rolling F/Bar(2nd)-- Cold Rolling -- Heat Treatment(Solution Annealing)-- Picking -- Levelling -- Surface Grinding & Polishing -- Machined F/Bar
Cold Rolling M/C
Grinding & Polishing M/C
Free cutting stainless steel flat bat for watch case.
Grade:
-
Chemical composition
C
Si
Mn
P
S
Ni
Cr
Mo
GRADE Spec.
316F2
0.8MAX
1.0MAX
2.0MAX
.20MAX
added
11/14
16/18
1.75/2.50
316LF
.03MAX
SAME AS OVER
Quality Control
Surface: 2B Finished.(Not No.1 Hot Rolled Finished)
Size Tolerance - Thickness: +0.1/-0mm, Width:
-
a) 316F2
b) 304
Fig.3) Comparison of broken chip shapes between 316F2 and 304.(3mm dia.drilled test.)
Fig.4) Gold Coating & 90° bend
-
Chemical composition
C
Si
Mn
P
S
Ni
Cr
Mo
GRADE Spec.
316F2
0.8MAX
1.0MAX
2.0MAX
.20MAX
added
11/14
16/18
1.75/2.50
316LF
.03MAX
SAME AS OVER
Quality Control
Surface: 2B Finished.(Not No.1 Hot Rolled Finished)
Size Tolerance - Thickness: +0.1/-0mm, Width:
-
a) 316F2
b) 304
Fig.3) Comparison of broken chip shapes between 316F2 and 304.(3mm dia.drilled test.)
Fig.4) Gold Coating & 90° bend
-
Certificate for 'EM'
Agency for Technology and Standards Ministry of Commerce, Industry & EnergyRepublic of