ABS resins are a family of thermoplastic resin made from three monomer of Acrylonitrile, Butadiene, Stylene. They have a number of specific grades such as general purpose, high impact, high heat resistance , flame retardant and a wide range of application in automotive, electronic/electronical, industrial, housing parts.
LKG (GENERAL PURPOSE)
LKI (HIGH IMPACT)
LKSH (SHEET EXTRUSION)
Application
LKG : Electric Home Appliances, General Merchandise, Tape recorders, Audio, Air-conditioner, Toys
LKI : Helmets, Pipe & Fittings, Mixer, Camera, Typewriter, Cash Resisters,Vacuum Cleaners
LKSH : Suitcase, Architecture Sheet, Refrigerator Doors
Properties
PROPERTIES
UNIT
TEST CONDITION
UNIT
ASTM
PC/ABS ALLOY
GRADE NO.
.
.
.
.
LKG
LKI01
LKI02
LKSH
TENSILE STRENGTH
Kg/cm2
.
D638
470
400
450
460
.
ELONGATION
% G/10min
.
D638
25
50
50
30
.
FLEXURAL STRENGTH
Kg/cm2
.
D790
720
570
720
750
.
FLEXURAL MODULES
Kg/cm2
.
Kg·cm/cm
D790
22,000
17,000
21,000
25,000
IZOD IMPACT STRENGTH
Kg·cm/cm
Notchecl 14"
.
D256
21
42
37
40
ROCKWELL HARDNESS
R-SCALE
.
%
D785
105
92
100
102
HEAT DEFLECTION TEMP
.
Unannealed 18.5km/cm2
Kg/cm2
D648
90
90
90
91
MELT FLOWINDEX
G/10min
220/10kg
Kg/cm2
D1238
35
12
20
6
VICAT SOFTENING TEMP
.
1kg
.
D1525
97
98
98
105
SPECIFIC GRAVITY
.
.
.
D792
1.05
1.05
1.05
1.05
CHARACTER- ISTICS
.
.
.
.
HighFlow
HighImpact
MediumImpact
extrusion
LKFR (FRAME RETARDANT)
LKFR resins are appropriate for the production of electric/electronic component and their various grades are developed according to flame retardant levels and characteristics.
LKH (HIGH HEAT RESISTANCE)
LKH resins have high heat resistance as well as superior physical properties such as impact strength, rigidity and process ability that they are suitable for automotive parts which require heat resistance.
LKFR : Monitor Case, TV, VTR, Printer, Fax and other electronic parts requiring flame retardant property.
LKH : Automobile interiors, Lamp Housing, Heater, Cluster Housing.
PROPERTIES
UNIT
TEST CONDITION
ASTM
PC/ABS ALLOY
GRADE NO.
.
.
.
LKH01
LKH02
LKH03
LKFR
TENSILE STRENGTH
Kg/cm2
.
D638
420
460
480
430
ELONGATION
%
50mm/cm
D638
30
28
20
20
FLEXURAL STRENGTH
Kg/cm2
.
D790
700
740
800
730
FLEXURAL MODULES
Kg/cm2
.
D790
20,000
23,000
25,000
24,000
IZOD IMPACT STRENGTH
Kg·cm/cm
Notchecl 1/4"
D256
22
18
12
20
ROCKWELL HARDNESS
R-SCALE
.
D785
100
104
109
100
HEAT DEFLECTION TEMP
Unannealed 18.5km/cm2
D648
95
104
108
78
MELT FLOWINDEX
G/10min
220/10kg
D1238
10
7
5
47
VICAT SOFTENING TEMP
.
D1525
110
125
130
87
SPECIFIC GRAVITY
.
.
D792
1.05
1.05
1.05
1.2
FLAMMABILITY
1/16 inch
UL-94
.
HB
HB
HB
HB
CHARACTER- ISTICS
.
.
.
Middle Impact Heat Resistance
High Heat Resistance
Super High Heat Resistance
Impact Flame Retardant
Share ABS in Social Media